Default Bending aluminum

Hello,

I am restoring a snowmobile and need to replace the tunnel on it. This is what a tunnel looks like on a snowmobile.



It's thinner aluminum, 16 gauge typically, bent at 90 degrees in a tight radius.
Searching online it seems manufacturers of snowmobiles will use 6061, the T6 version. Though that seems impossible to bend.
It seems like manufacturers may be bending the 6061 tunnels into shape then heat treating it into T6. This does not seem practical for a garage fabricator like me.

Using 5032 would be easier, though it is much softer than 6061.
What would be your thoughts? 6061 comes in a T0 version, would there be any benefits to using 6061-T0 over 5052?
Would 5032 just suffice for this application?

Thanks,
JS
Reply With Quote
  #2  
Old 09-16-2024, 12:11 PM
mccutter's Avatar
mccutter mccutter is offline
Do I have a life?
 
Join Date: Mar 2006
Location: Central Florida
Posts: 11,652
Default

6063, if you can find it, is more "bendable". I would imagine the mfg has a giant press to stamp the tunnel from.

BTW, Welcome Aboard!
__________________

TA Arcmaster 185 w/tig/stick kit
MillerMatic 252 w/3rd gen 30A
MM140 w/o AS, w/CO2
Hobart (Miller) 625 plasma
Hobart 250ci plasma
Victor O/A (always ready, but bored)
HF 80 lunchbox w/tig
45ACP Black Talons for those stubborn jobs...
Reply With Quote
  #3  
Old 09-16-2024, 02:01 PM
LKeithR's Avatar
LKeithR LKeithR is offline
Hey...wait...is there a prize?
 
Join Date: Aug 2011
Location: Langley, B.C.
Posts: 5,762
Default

As has been mentioned, bending 6061 to that tight of a radius just won't work. As far as I know you're going to have difficulty finding sheet in a 6063 alloy, it's generally used for extrusions like pipe, angles, channels, etc. While 5052 is the go to alloy for bending I would look for some 5086, it's bendable and it will give you a little more strength. You might have to go with a slightly larger radius for the bends.

If you have to use 5052 or 5086 step up the thickness by one or two guages, you'll gain some strength without gaining significant weight. If your current material measures 1/16" it's probably 14 GA (.0641), stepping up to 12 GA (.0808) will make a difference...
__________________
Keith

Measure twice and cut once...or...wait, was that the other way around?
Reply With Quote
  #4  
Old 09-16-2024, 09:20 PM
arizonian's Avatar
arizonian arizonian is offline
Elite Member
 
Join Date: Jul 2007
Location: Tucson, Arizona
Posts: 2,417
Default

I am not the aluminum guy, but I did sleep at home last night.

One thing to consider when you do get some material is to vary the radius of the bend on trial bends. You may get cracking if you try to go too tight of a radius. If so, then make the radius larger and try again.

Leaf brake, press brake or finger brake? They all have some means to adjust the radius.
__________________
Bill in sunny Tucson

I believe in gun control.

Gun Control: The ability to consistently hit what you are aiming at.

Weldor by choice, engineer by necessity.
Reply With Quote
Reply

Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump

Web Search:

All times are GMT -5. The time now is 05:06 PM.


Powered by vBulletin® Version 3.8.11
Copyright ©2000 - 2024, vBulletin Solutions Inc.