Default Dont fear the Titanium

I have a few jobs to do that require titanium. I asked advice here as I had never worked with it before. I was expecting a tough job...I was in for a surprise.

I picked up some 6al-4v off ebay. I have a baby 10" lathe that is WWII vintage so I was a little worried about that. My insert selection is limited so I decided to just give the coated TCMT's I have a shot.
I plowed off into it with a fast feed as suggested. It cut beautiful with a good finish. I had some stringy chips that I am sure the correct insert would have taken care of. My coolant setup was a mess so I decided to give it a shot dry. That really was no problem at all! As long as I fed hard I could take pretty decent cuts for my machine without bogging at all.

So far it has been a very painless experience. If you can turn stainless then dont be afraid of titanium at all.
__________________
Director of Cryptography-Upstate NY Division
Reply With Quote
  #2  
Old 06-16-2008, 11:18 PM
pumpertruck's Avatar
pumpertruck pumpertruck is offline
Spinner of Wood
 
Join Date: Apr 2008
Location: Pothole Hell, Anoka county, MN
Posts: 3,406
Default

Just don't get a fire started. Worse than magnesium.
__________________
Shorter of breath and one day closer to death.....


http://www.ibrbsantas.org/
Reply With Quote
  #3  
Old 06-17-2008, 08:13 PM
markct markct is offline
Member
 
Join Date: Nov 2004
Location: northfield, ct
Posts: 82
Send a message via Yahoo to markct
Default

yea that was my first thought when i read his post! thats my big fear of titanium, had it catch fire once in the chip pan, basicly just let it burn out, fire extinguisher, co2 then dry chemical, didnt help much
Reply With Quote
  #4  
Old 06-18-2008, 04:21 AM
Cavalry's Avatar
Cavalry Cavalry is offline
Below Wholesale
 
Join Date: Jul 2005
Location: Evil Empire State
Posts: 9,041
Default

I played with the chips a little, after I was done. It took quite a bit of O/A to get them going. IMO Mg puts out a hotter fire? good times regardless!
__________________
Director of Cryptography-Upstate NY Division
Reply With Quote
  #5  
Old 06-18-2008, 01:47 PM
precisionworks's Avatar
precisionworks precisionworks is offline
American Tools Keep Americans Working
 
Join Date: Oct 2005
Location: Benton, IL
Posts: 3,177
Default

If you operations are external (OD turning, facing, threading, surface milling, etc.) air coolant, or even just an air pipe, will help. Internal ops (like drilling deep holes) are a bear - that's where liquid coolant shines. A machinist who turns Ti posted on the CPF forum, showing how he set up a liquid coolant system for his SB Heavy Ten. Says that drills that used to get so hot that they'd turn blue, now last & last with the liquid cool.
__________________
Barry Milton - Please email or PayPal through PrecisionWorks.co
PM's are disabled
Reply With Quote
  #6  
Old 06-18-2008, 03:11 PM
Cavalry's Avatar
Cavalry Cavalry is offline
Below Wholesale
 
Join Date: Jul 2005
Location: Evil Empire State
Posts: 9,041
Default

I have the coolant. My lathe was just never set up for such a thing. I plan on getting a better setup. should help tool life in general
__________________
Director of Cryptography-Upstate NY Division
Reply With Quote
Reply

Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump

Web Search:

All times are GMT -5. The time now is 06:23 AM.


Powered by vBulletin® Version 3.8.11
Copyright ©2000 - 2024, vBulletin Solutions Inc.